X07Cr21Mn6Ni2N
2023-07-24 14:57:56 Origin： Remark：0 Click：
IS 1570-5 Austenitic Steel X07Cr21Mn6Ni2N Round bar, flat bar, plate, forgings X07Cr21Mn6Ni2N ESR melted, Cold working or rough turned machining.
MATERIAL TECHNICAL DATASHEET - Grade X07Cr21Mn6Ni2N
Official Test Report: issued by TUV - SGS - BV
Special Melting Practice - BEF + AOD / + ESR
HS Code For Customs - 72221100 / 72221900 / 72222000
Inventory on hand - Round bar Diam. 70 / 100mm
Material Specifications - IS 1570-5 (1985 / 2004)
Official Test Report: issued by TUV - SGS - BV
Special Melting Practice - BEF + AOD / + ESR
HS Code For Customs - 72221100 / 72221900 / 72222000
Inventory on hand - Round bar Diam. 70 / 100mm
Material Specifications - IS 1570-5 (1985 / 2004)
MAIN CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.12
Silicon, Si (％): 0.45 ~ 0.85
Manganese, Mn (％): 5.50 ~ 7.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 20.0 ~ 22.0
Nickel, Ni (％): 1.40 ~ 1.90
Molybdenum, Mo (％): -
Nitrogen, N (%): -
Carbon, C (％): ≤ 0.12
Silicon, Si (％): 0.45 ~ 0.85
Manganese, Mn (％): 5.50 ~ 7.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 20.0 ~ 22.0
Nickel, Ni (％): 1.40 ~ 1.90
Molybdenum, Mo (％): -
Nitrogen, N (%): -
MECHANICAL PROPERTY AT ROOM TEMPERATURE
Forms: Round bar, flat bar, forgings and plate
Annealing temp: 1050 ℃, water, oil cooling.
Tensile strength, σb/≥ MPa: 655 max.
Yield strength, σ0.2/MPa: 310
Elongation, δ ≥(％): 35.0
Reduction of area, ф ≥ (％): -
Hardness via annealing /HBW: 245 max.
Forms: Round bar, flat bar, forgings and plate
Annealing temp: 1050 ℃, water, oil cooling.
Tensile strength, σb/≥ MPa: 655 max.
Yield strength, σ0.2/MPa: 310
Elongation, δ ≥(％): 35.0
Reduction of area, ф ≥ (％): -
Hardness via annealing /HBW: 245 max.
PRODUCT DESCRIPTION
The alloy is usually produced by EAF +LF + VD / AOD / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + Stress relief annealing. Solution treatment + aged
The alloy is usually produced by EAF +LF + VD / AOD / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + Stress relief annealing. Solution treatment + aged
PROFILE & DIMENSIONS & SERVICE
Round bar (diameter): 5.5mm to 200mm
Square bar / Flat bar: 10mm to 550mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T10 ~ 400mm X W70 ~ 1200mm X Lmm
Sheet steel via cold rolled: T0.5 - 6mm X W60 ~ 1220mm X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 1200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Round bar (diameter): 5.5mm to 200mm
Square bar / Flat bar: 10mm to 550mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T10 ~ 400mm X W70 ~ 1200mm X Lmm
Sheet steel via cold rolled: T0.5 - 6mm X W60 ~ 1220mm X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 1200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.