7Cr19Ni11TiH
2023-09-21 09:22:05 Origin： Remark：0 Click：
IS 1570-5 Material Specification Austenitic Steel 7Cr19Ni11TiH Round bar, flat bar, plate and forgings Instock 7Cr19Ni11TiH Heat treatment, Cold worked.
MATERIAL TECHNICAL DATASHEET - Grade 7Cr19Ni11TiH
Official Test Report: issued by TUV - SGS - BV
Special Melting Practice - BEF + AOD / + ESR
HS Code For Customs - 72221100 / 72221900 / 72222000
Available stock on hand - Round bar Diam. 3.0 ~ 220mm
Material Specifications - IS 1570-5 (1985 / 2004)
Official Test Report: issued by TUV - SGS - BV
Special Melting Practice - BEF + AOD / + ESR
HS Code For Customs - 72221100 / 72221900 / 72222000
Available stock on hand - Round bar Diam. 3.0 ~ 220mm
Material Specifications - IS 1570-5 (1985 / 2004)
MAIN CHEMICAL ELEMENTS (mass weight - %)
Carbon, C (％): 0.04 ~ 0.10
Silicon, Si (％): 0.20 ~ 0.80
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 17.0 ~ 20.0
Nickel, Ni (％): 9.00 ~ 13.0
Molybdenum, Mo (％): -
Titanium, Ti (%): 4 X C ~ 0.60.
Carbon, C (％): 0.04 ~ 0.10
Silicon, Si (％): 0.20 ~ 0.80
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 17.0 ~ 20.0
Nickel, Ni (％): 9.00 ~ 13.0
Molybdenum, Mo (％): -
Titanium, Ti (%): 4 X C ~ 0.60.
MECHANICAL PROPERTY AT ROOM TEMPERATURE
Forms: Round bar, wire rod, flat bar, forgings and plate
Annealing temp: 1050 ℃, water or oil cooling.
Tensile strength, σb/≥ MPa: 510 ~ 710
Yield strength, σ0.2/MPa: 195
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness via annealing /HBW: 207 max.
Forms: Round bar, wire rod, flat bar, forgings and plate
Annealing temp: 1050 ℃, water or oil cooling.
Tensile strength, σb/≥ MPa: 510 ~ 710
Yield strength, σ0.2/MPa: 195
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness via annealing /HBW: 207 max.
PROFILE & DIMENSIONS & SERVICE
Round bar & Disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 10mm to 1200mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T10 ~ 400mm X W70 ~ 1200mm X Lmm
Sheet steel via cold rolled: T0.5 - 6mm X W60 ~ 1500mm X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 1000mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Round bar & Disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 10mm to 1200mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T10 ~ 400mm X W70 ~ 1200mm X Lmm
Sheet steel via cold rolled: T0.5 - 6mm X W60 ~ 1500mm X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 1000mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.