X8CrMnN19-19
2023-12-19 08:10:35 Origin： Remark：0 Click：
DIN SEW 390 (1991) Specification Austenitic Nonmagnetic Steel X8CrMnN19-19 Round bar, Flat bar, and X8CrMnN19-19 Stock Available, Heat treatment, 100% UT
Official Test Certificate: issued by TUV - SGS - BV
RAW MATERIAL DATASHEET - Grade DIN 1.3815 X8CrMnN19-19
Material Catetory - Non-magnetic stainless steel and alloy
Material Specifications - DIN SEW 390 (1991)
Stock Available - Round bar Diameter 55 ~ 180mm
Main Chemical Elements (mass weight - %)
Carbon, C (％): ≤ 0.12
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 17.5 ~ 20.0
Phosphorus, P (％) ≤: 0.050
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 17.5 ~ 20.0
Nickel, Ni (％): ≤ 0.30
Vanadium, V (％): ≤ 0.20
Aluminum, Al (％): ≤ 0.10
Niobium, Nb (％): ≤ 0.25
Nitrogen, N (％): ≥ 0.55
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 850℃
Solution treatment temperature: 1050 ℃
Tensile strength, σb≥ /MPa: 500 ~ 750
Yield strength, σ0.2 ≥/MPa: 285
Elongation, δ≥(％): 15.0
Impact strength, Akv ≥/J: -
PRODUCT FORMS & DIMENSIONS
Round bar & Disc (diameter): 5.5mm to 600mm
Square bar / flat bar: 10mm to 550mm
Length: fixed length, random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T10 - 400mm X W15 - 1000mm X L1000 - 5000mm
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.