X8CrMnN20-10
2024-01-08 08:45:35 Origin: Remark:0 Click:
Official Test Certificate: issued by TUV - SGS - BV
RAW MATERIAL DATASHEET - Grade DIN X8CrMnN20-10
Material Catetory - Non-magnetic stainless steel and alloy
Material Specifications - DIN SEW 390 (1991)
Stock Available - Round bar Diameter 20 ~ 210mm
Main Chemical Elements (mass weight - %)
Carbon, C (%): ≤ 0.12
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): 9.00 ~ 10.0
Phosphorus, P (%) ≤: 0.050
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 18.0 ~ 20.0
Nickel, Ni (%): ≤ 1.00
Molybdenum, Mo (%): ≤ 1.00
Nitrogen, N (%): 0.40 ~ 0.65
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 850℃
Solution treatment temperature: 1050 ℃
Tensile strength, σb≥ /MPa: 500 ~ 750
Yield strength, σ0.2 ≥/MPa: 285
Elongation, δ≥(%): 15.0
Impact strength, Akv ≥/J: -
PRODUCT FORMS & DIMENSIONS
Round bar & Disc (diameter): 5.5mm to 700mm
Square bar / flat bar: 10mm to 550mm
Length: fixed length, random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T10 - 400mm X W15 - 1000mm X L1000 - 5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search:X8CrMnN20-10
Previous page:XT78W18Cr4V1
Last page:40C10S18 & 40S18
Total list
Monthly rank
- 39ASTM A565 Gr.616HT
- 37X35CrMo17
- 30ASTM A638 Gr.660
- 28EN 58A
- 27Z10CNT18-11
- 26SAE 30304
- 26ASTM A538 / AMS 6514
- 26AISI 306
- 25Z15CN17-03
- 2410705MBU