10Cr36Mo10H
2024-01-12 08:35:05 Origin: Remark:0 Click:
IS 1570-5 Material Specification Refractory Steel 10Cr36Mo10H Round bar, flat bar, plate and forgings Instock 10Cr36Mo10H Heat treatment, Cold finished
MATERIAL TECHNICAL DATASHEET - Grade 10Cr36Mo10H
Official Test Report: issued by TUV - SGS - BV
Special Melting Practice - BEF + AOD / + ESR
HS Code For Customs - 72221100 / 72221900 / 72222000
Available stock on hand - Round bar Diam. 25 ~ 170mm
Material Specifications - refractory Steel IS 1570-5 (1985 / 2004)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.15
Silicon, Si (%): 0.25 ~ 1.00
Manganese, Mn (%): 0.30 ~ 0.60
Phosphorus, P (%) ≤: 0.040
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 8.00 ~ 10.0
Nickel, Ni (%): -
Molybdenum, Mo (%): 0.90 ~ 1.15
Ferrum, Fe (%): -
Official Test Report: issued by TUV - SGS - BV
Special Melting Practice - BEF + AOD / + ESR
HS Code For Customs - 72221100 / 72221900 / 72222000
Available stock on hand - Round bar Diam. 25 ~ 170mm
Material Specifications - refractory Steel IS 1570-5 (1985 / 2004)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.15
Silicon, Si (%): 0.25 ~ 1.00
Manganese, Mn (%): 0.30 ~ 0.60
Phosphorus, P (%) ≤: 0.040
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 8.00 ~ 10.0
Nickel, Ni (%): -
Molybdenum, Mo (%): 0.90 ~ 1.15
Ferrum, Fe (%): -
MECHANICAL PROPERTY AT ROOM TEMPERATURE
Quenching temp: 920 ~ 980 ℃, water or oil cooling, tempering 680℃, air cooling.
Tensile strength, σb/≥ MPa: 585
Yield strength, σ0.2/MPa: 415
Elongation, δ ≥(%): 20.0
Reduction of area, ф ≥ (%): -
Hardness via annealing /HBW: 215
Quenching temp: 920 ~ 980 ℃, water or oil cooling, tempering 680℃, air cooling.
Tensile strength, σb/≥ MPa: 585
Yield strength, σ0.2/MPa: 415
Elongation, δ ≥(%): 20.0
Reduction of area, ф ≥ (%): -
Hardness via annealing /HBW: 215
PRODUCT DESCRIPTION
The alloy is usually produced by EAF +LF + VD / AOD / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + Stress relief annealing. Solution treatment + aged
The alloy is usually produced by EAF +LF + VD / AOD / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + Stress relief annealing. Solution treatment + aged
PROFILE & DIMENSIONS & SERVICE
Round bar & Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 610mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T10 ~ 400mm X W70 ~ 1000mm X Lmm
Sheet steel via cold rolled: T0.5 - 6mm X W60 ~ 1000mm X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 1000mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Round bar & Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 610mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T10 ~ 400mm X W70 ~ 1000mm X Lmm
Sheet steel via cold rolled: T0.5 - 6mm X W60 ~ 1000mm X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 1000mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.