MT 316
2026-07-04 09:13:08 Origin： Remark：0 Click：
ASTM A511/511M - 12 specification for seamless stainless steel mechanical tubing MT 316 round bar, flat bar, plate, forgings MT 316 stock available, 1040℃ annealed solution treated
TECHNICAL DATA SHEET - MT 316
Material specifications: ASTM A511 / 511M - 12
Material category: austenitic type 17.0Cr - 12.0Ni - 2.0Mo base steel
Official test certificate: issued by TUV - SGS - CNAS
Stock available: round bar 6.0 ~ 300 mm
PRODUCT DESCRIPTION
MT 316 is usually produced by EAF / AOD / BEF followed by electro-slag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied in the annealed, peeled condition.
Final heat treatment - annealing.
Material category: austenitic type 17.0Cr - 12.0Ni - 2.0Mo base steel
Official test certificate: issued by TUV - SGS - CNAS
Stock available: round bar 6.0 ~ 300 mm
PRODUCT DESCRIPTION
MT 316 is usually produced by EAF / AOD / BEF followed by electro-slag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied in the annealed, peeled condition.
Final heat treatment - annealing.
PROFILES AND DIMENSIONS
Rod / round bar / disc (diameter): 6.0 ~ 800 mm
Square bar & flat bar: 10 ~ 800 mm
Length: random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T3 ~ 300 X W 15 ~ 1500 X L mm
Sheet steel via cold rolled: T 0.5 ~ 3 X W15 ~ 1000 X L mm
Steel strip via cold rolled: T 0.3 ~ 3.0 X W 10 ~ 300 X L mm (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Carbon, C (％): ≤ 0.08
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％): ≤ 0.040
Sulfur, S (％): ≤ 0.030
Sulfur, S (％): ≤ 0.030
Silicon, Si (％): ≤ 1.00
Nickel, Ni (％): 11.0 ~ 14.0
Chromium, Cr (％): 16.0 ~ 18.0
Chromium, Cr (％): 16.0 ~ 18.0
Molybdenum, Mo (％): 2.00 ~ 3.00
Titanium, Ti (%): -
Ferrum, Fe (%): reaminder.
MECHANICAL PROPERTY AT ROOM TEMPERATURE
Heat treatment practice: solution annealing 1040 ℃ rapid cooling
Tensile strength, Rm ≥ MPa: 515
Yield strength, Rp0.2 ≥ MPa: 205
Yield strength, Rp0.2 ≥ MPa: 205
Elongation, A5 ≥ (％): 35.0
Reduction of area, Z ≥ (％): -
Hardness via heat treatment / HBW.: HRB 90 max.
Reduction of area, Z ≥ (％): -
Hardness via heat treatment / HBW.: HRB 90 max.
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years focus on special steel manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
20+ years focus on special steel manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you are interested in our products or services, or would like to learn more about us, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers or sales department.
JIANGYOU LONGHAI SPECIAL STEEL CO.,LTD
ISO 9001-2015 Certified by UKAS, UICC
Raw Material Stock Available
Custom 450 / GD450 / XM-25 (S45000), 403 ESR, AISI 616 / 422 ESR, B50A365 / 403Cb+
17-4PH / 630, M-152 / 1.4938 / S151D, FV520B / S143 / 1.4594. X22CrMoV12-1
13Х11Н2B2MФ / AE961W, 11Х11Н2B2MФ / 16Х11Н2B2MФ
AISI 615 / S41800, 15-5PH / XM-12 (S15500), A-286 AISI 660 / S66286
10705BU, 10705MBU, 10705AJ, S132, S131, S111, S159, S154
Total list
Monthly rank
- 19N06102
- 19Z15CN24-13
- 16ASTM 301
- 15STS321
- 15X1CrNiMoCu12-5-2
- 15S41425
- 141.6359
- 14Z4CNUD17-11-03FF
- 14F316L
- 14BS S126