S44023
2014-10-27 10:23:40 Origin： Remark：0 Click：
Technical specifications of UNS S44023 Martensite steel - Chemical composition, mechanical properties from steelmaking, forging, rolling, heat treatment, cold working.
MATERIAL DATA SHEET - AISI 440FSe & UNS S44023
MATERIAL CATEGORY: Martensite type 17Cr-Se
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.95 ~ 1.20
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.25
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 16.0 ~ 18.0
Nickel, Ni (％): ≤ 0.75
Molybdenum, Mo (％): ≤ 0.60
Other (％): Se ≥ 0.15
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.25
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 16.0 ~ 18.0
Nickel, Ni (％): ≤ 0.75
Molybdenum, Mo (％): ≤ 0.60
Other (％): Se ≥ 0.15
MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T)
Form: bar
Condition: annealing
σb/MPa: 760
σ0.2/MPa: 450
σ0.2/MPa: 450
δ (％): 14
ф (％): -
Hardness | HRB: 97
ф (％): -
Hardness | HRB: 97
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Product engineers, Email: sales@ccsteels.com