1.4105 / X6CrMoS17
2025-04-14 16:00:00 Origin： Remark：0 Click：
Ferritic steel 1.4105 Shaft, Inventory X6CrMoS17 Flat bar, Stockist 1.4105 round bars Properties from steelmaking, hot forging/rolling, heat treatment
TECHNICAL DATA SHEET - X6CrMoS17 & WS 1.4105
MATERIAL CATEGORY: Ferritic type
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - solution treatment / QT.
The alloy is usually produced by AOD / EAF. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - solution treatment / QT.
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 1.50
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.15 ~ 0.35
Chromium, Cr (％): 16.0 ~ 18.0
Nickel, Ni (％): -
Molybdenum, Mo (％): 0.20 ~ 0.60
Silicon, Si (％): ≤ 1.50
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.15 ~ 0.35
Chromium, Cr (％): 16.0 ~ 18.0
Nickel, Ni (％): -
Molybdenum, Mo (％): 0.20 ~ 0.60
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealed
Thickness / mm: 100
Thickness / mm: 100
Tensile strength, Rm / MPa: 430~630
Yield strength, Rpσ0.2 ≥ MPa: 250
Elongation, δ5 ≥ (％): 20
Yield strength, Rpσ0.2 ≥ MPa: 250
Elongation, δ5 ≥ (％): 20
Reduction of area, ψ ≥ (％): -
Akv ≥ J: -
Hardness HBS30: 200
Akv ≥ J: -
Hardness HBS30: 200
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Heat treatment temperature and cooling methods|annealing: 750 ~ 850 air/water cooling
Heat treatment temperature and cooling methods|quenching: -
Heat treatment temperature and cooling methods|tempering: -
Condition: annealed
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 230
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 215
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 215
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 205
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 195
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 195
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shaft, and other different shapes based on OEM.
Medical equipment.
Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut.
Pressure vessel.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut.
Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.- Email: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.- Email: sales@ccsteels.com
Total list
Monthly rank
- 28Z15CN17-03
- 20ASTM A565 type 616HT
- 20N06102
- 19X8CrMnN18-18
- 18X35CrMo17
- 17Z8CND17-04
- 15X11CrMo12-1
- 15X2Cr11 / 1.4003
- 14Z8CND17-04 QT1100
- 14P550