X20CrMo13
2025-10-02 07:10:00 Origin： Remark：0 Click：
Martensistic steel X20CrMo13 cold rolled strip, round bar X20CrMo13 flat bar, peeled properties from steelmaking, Hot forged & rolled, heat treated
TECHNICAL DATA SHEET - DIN X20CrMo13
Material cateogry - Martensitic and precipitation hardening corrosion resisting steels
Material specifications - DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297
Typical chemical compositions (mass fraction %)
Carbon, C (％): 0.17 ~ 0.22
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 12.0 ~ 14.0
Nickel,Ni (％): ≤ 1.00
Molybdenum, Mo (％): 0.90 ~ 1.30
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 12.0 ~ 14.0
Nickel,Ni (％): ≤ 1.00
Molybdenum, Mo (％): 0.90 ~ 1.30
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: heat treatment
Thickness/mm:-
Thickness/mm:-
Tensile strength, σb / MPa: 750~900
Yield strength, σ0.2 ≥ MPa: 550
Elongation, δ5 ≥ (％): 14.0
Yield strength, σ0.2 ≥ MPa: 550
Elongation, δ5 ≥ (％): 14.0
Reduction of area, ψ ≥ (％): 50.0
Impact strength, Akv ≥ J: 25
Hardness HBS30: 220 ~ 280
Impact strength, Akv ≥ J: 25
Hardness HBS30: 220 ~ 280
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Heat treatment temperature and cooling methods|annealing: 750 ~ 850 furnace cooled
Heat treatment temperature and cooling methods|quenching: 950~1000 oil cooled
Heat treatment temperature and cooling methods|tempering: 650~750
Condition: HT
High temperature yield strength σ0.2/ MPa ≥ MPa, at below temp /℃ | 100: 520
High temperature yield strength σ0.2/ MPa ≥ MPa, at below temp /℃ | 200: 500
High temperature yield strength σ0.2/ MPa ≥ MPa, at below temp /℃ | 200: 500
High temperature yield strength σ0.2/ MPa ≥ MPa, at below temp /℃ | 300: 480
High temperature yield strength σ0.2/ MPa ≥ MPa, at below temp /℃ | 400: 410
High temperature yield strength σ0.2/ MPa ≥ MPa, at below temp /℃ | 400: 410
High temperature yield strength σ0.2/ MPa ≥ MPa, at below temp /℃ | 500: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolt, nut, and pressure vessel
Mechanical parts used in the condition of corrosion resistance
Bolt, nut, and pressure vessel
PRODUCT PROFILE & DIMENSIONS
Round bar / rod / disc (diameter): 6.0 to 850mm
Square bar / flat bar: 8 to 600mm
Round bar / rod / disc (diameter): 6.0 to 850mm
Square bar / flat bar: 8 to 600mm
Length: random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400 X W50 - 1000 X L1000 ~ 5000mm
Sheet steel via cold rolled: T0.5 - 6 X W60 - 1000 X L1000 - 2000mm
Steel strip via cold rolled: T0.4 - 3 X W5 - 200 X L mm (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Pipes / Tubings: OD30 - 1300mm, with wall thickness ranging from 15 to 350 mm.
Pipes / Tubings: OD30 - 1300mm, with wall thickness ranging from 15 to 350 mm.
ADVANTAGE & SUPERIOR SERVICE
17+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com
17+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com
Hot search：X20CrMo13
Previous page：1.4117 / X38CrMoV15
Last page：1.4120
Total list
Monthly rank
- 43Z15CN17-03
- 25Z8CND17-04
- 24X2Cr11 / 1.4003
- 21Z3CN18-10
- 19FV535
- 18X10CrNiW17-13-3
- 1418Cr-18Mn
- 14Magnadur 601
- 14ASTM A538 / AMS 6514
- 13P550