Haynes HR-120 / N08120
2016-09-24 15:05:21 Origin： Remark：0 Click：
Standard specification for Nickel - Iron - Chromium alloy rod and bar HR120 / UNS N08120 data sheet, N08120 Chemical compositions, N08120 mechanical properties from Steel making, ESR melted, Blooming, N084120 Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. Technical specification ASTM B408 - 2006.
MATERIAL STANDARD SPECIFICATION - HR 120 & ASTM B408 GRADE N08120
TECHNICAL SPECIFICATION: ASTM B408 - 2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Nickel - Iron - Chromium alloy rod and bar
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.02 ~ 0.10
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％) ≤: 0.035
S (％) ≤: 0.030
Cr (％): 23.0 ~ 27.0
Ni (％): 35.0 ~ 39.0
Mo (％): ≤ 2.50
Nb (%): 0.40 ~ 0.90
Ti (%): ≤ 0.20
Cu (%): ≤ 0.50
Al (%): ≤ 0.40
Al (%): ≤ 0.40
N (%): 0.15 ~ 0.30
B (%): ≤ 0.010
W (%): ≤ 2.50
Co (%): ≤ 3.00
Fe (%): Remainder
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Form: round bar
Condition: annealed, at 1177 Deg. min.
Tensile strength,σb/≥ MPa: 621
Yield strength, σ0.2/≥ MPa: 276
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness | HRC: -
Co (%): ≤ 3.00
Fe (%): Remainder
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Form: round bar
Condition: annealed, at 1177 Deg. min.
Tensile strength,σb/≥ MPa: 621
Yield strength, σ0.2/≥ MPa: 276
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness | HRC: -
Service temperature: above 593 Deg.
FORMS AND SHAPES
Round bar (Diameter): 0.50mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
FORMS AND SHAPES
Round bar (Diameter): 0.50mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. - Email: lh.steel@hotmail.com
Hot search：Haynes HR-120/N08120
Previous page：ASTM B408 N08120
Last page：ASTM B408 N08800
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17