ASTM A453 Gr.668B Stockist, ASTM A453 Gr.668B Equivalent Steel
Home > Superalloy > Text

ASTM A453 Gr.668B
2016-10-18 13:16:28   Origin:   Remark:0 Click:

Material standard specification for high-temperature bolting,Grade 668B with expansion coefficients comparable to austenitic stainless steel ASTM A453 GR.668B datasheet,ASTM A453 668B Chemical compositions,ASTM A453 Gr 668B mechanical properties from Steel making, ESR, hot Blooming, Forging, Hot rolling, Heat treatment, Straightening,Ultrasonic test,Cold working or Machined. All of these materials conform to Military standard, nuclear power. Technical specification ASTM A453 - 2011
TECHNICAL SPECIFICATION - ASTM A453 GRADE 668B

TECHNICAL SPECIFICATION: ASTM A453 - 2011
OFFICIAL TEST CERTIFICATE: issued by
TUV - SGSBV

MATERIAL CATEGORY:  high-temperature bolting, with expansion coefficients comparable to austenitic stainless steel
CHEMICAL COMPOSITION (WEIGHT %)
C (%):     ≤ 0.08
Si (%):     ≤ 1.00
Mn (%):   ≤ 2.00
P (%) ≤:  0.040
S (%) ≤:  0.030
Cr (%):    13.5 ~ 16.0
Ni (%):    17.5 ~ 21.5
Mo (%):   ≤ 1.50
W (%):    -
Ti (%):    2.20 ~ 2.80
Nb (%):   -
Al (%):    ≤ 0.50
V (%):     ≤ 0.50
B (%):     0.001 ~ 0.010
Cu (%):   -
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Form: rod and bar
Condition: solution treated 980 +/-14 Deg. hold 1h, liquid quench. hardening treatment 720 -/+14 Deg. hold 16h, air cool 
Tensile strength,σb/≥ MPa: 895
Yield strength, σ0.2/≥ MPa: 585
Elongation, δ ≥(%): 15.0
Reduction of area, ф ≥ (%): 18.0
Hardness | HBW: 248 ~  341
Hardness | HRC: 24 ~ 37
STRESS RUPTURE REQUIREMENT
Test temperature: 650 Deg.
Stress /MPa: 515 min.
Time to rupture: 100h min.
Elongtation, (%): 3
TYPICAL APPLICATIONS 
Starndard specification for high-temperature bolting, with expansion coefficients comparable to austenitic stainless steel with yield strength ranging from 345 to 827 MPa for use in high-temperature service such as fasteners for pressure vessel and valve flanges.
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Gas turbine blade
Fuel nozzle
These materials must stand up to high heat, extreme oxidation potential and recycling.
FORMS AND SHAPES
Round bar (Diameter): 2.0mm to 400mm
Square bar / Flat bar: 3mm to 500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.

TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail:
lh.steel@hotmail.com    

Hot search:ASTM A453 Gr.668B

Previous page:A453 Gr S66285
Last page:N07022 type 1

Share to: