Valve body 17-4PH Round bar AMS 5643 Forgings, AMS 5643 Flat bar 17-4PH Wire ESR refined, Hot forging/rolling, Heat treated, 100% Ultrasonic flaw detection test, Cold worked.
RAW MATERIAL DESIGNATION - 17-4PH & S17400
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: high-tensile superalloy & Precipitation hardening steel
INVENTORY & STOCK LIST- Round bar diameter 5.5 ~ 300mm, ESR ingot, forging blank
HS CODE FOR CUSTOMS - 72221100 / 72221900 / 72222000 / 72223000
CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (%): ≤ 0.07
Silicon, Si (%): ≤ 0.40
Manganese, Mn (%): ≤ 0.60
Phosphorus, P (%) ≤: 0.025
Sulfur, S (%) ≤: 0.010
Chromium, Cr (%): 15.0 ~ 16.0
Nickel, Ni (%): 3.80 ~ 4.50
Molybdenum, Mo (%): -
Manganese, Mn (%): ≤ 0.60
Phosphorus, P (%) ≤: 0.025
Sulfur, S (%) ≤: 0.010
Chromium, Cr (%): 15.0 ~ 16.0
Nickel, Ni (%): 3.80 ~ 4.50
Molybdenum, Mo (%): -
Niobium, Nb (%): 0.15 ~ 0.45
Copper, Cu (%): 3.00 ~ 3.70
Ferrum, Fe (%): balance
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: TH1025, H1100, H1050, H900
Tensile strength, σb ≥ MPa: 1070
Yield strength, σ0.2 ≥ MPa: 1000
Elonghation, δ5 ≥ (%): 12.0
Reduction of area, ф ≥ (%): 45.0
Hardness | HB: 35HRC min.
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
PRODUCT DESCRIPTION
The alloy 17-4PH / AISI 630 is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
The alloy 17-4PH / AISI 630 is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND DIMENSIONS
Rod / round bar / disc (diameter): 5.5mm to 950mm
Square bar / flat bar: 8mm to 600mm
Heavy / middle plate via hot rolled: T60 - 400mm X W70 - 1500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Square bar / flat bar: 8mm to 600mm
Heavy / middle plate via hot rolled: T60 - 400mm X W70 - 1500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Previous page:N10002
Last page:Hastelloy C
Total list
Monthly rank
- 2710705BU
- 18Carpenter 20 Mo 4
- 10AMS 5833
- 10FSX-414
- 10X12CrNiMoV12-2
- 9XM-25
- 7Aquamet 22
- 7Custom 475
- 6AF-1410
- 6AMS 5719