Hastelloy C Stockist, Hastelloy C Equivalent Steel
Home > Superalloy > Text

Hastelloy C
2021-01-28 11:31:22   Origin:   Remark:0 Click:

Specifications Hastelloy C datasheet, Hastelloy C Chemical, Hastelloy C Properties Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL STANDARDS DATASHEET - Hastelloy C

MATERIAL CATEGORY - high alloy stainless Steel Series
TECHNICAL SPECIFICATION - AMS 5530G
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (%):     ≤ 0.08
Si (%):     ≤ 1.00
Mn (%):   ≤ 1.00
P (%)≤:   0.035
S (%)≤:   0.025
Cr (%):    14.5 ~ 16.5
Ni (%):    Remainder
Mo (%):   15.0 ~ 17.0
W (%):    3.00 ~ 4.50
Co (%):   ≤ 2.50
V (%):     0.35 Min.
Fe (%):   4.00 ~ 7.00
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Form: plate, sheet, strip
Tensile strength, σb/MPa: 620
Yield strength, σ0.2/MPa: 310
Elongation, δ(%): 20.0
Reduction of area, ф(%):  -
Hardness (HB): HRC 25 Max.
MELTING PROCESS & APPLICATION
This
alloy is generally smelt in Electric Arc Furnace (EAF), BEF (AOD) & VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 400mm
Square bar / Flat bar: 10mm to 650mm
Wire rod: 1.0mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 650mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM. 
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail:
sales@ccsteels.com.

Hot search:Hastelloy C

Previous page:17-4PH / AMS 5643
Last page:T41902

Share to: