Technical specification of DIN X5CrNiMoTi15-2 Stainless steel round bar, flat bar, plate, sheet, property from steelmaking, hot forged, rolled, heat treated
TECHNICAL DATA SHEET - X5CrNiMoTi15-2 & 1.4589
Material category: Ferritic corrosion resisting steels
Product description
The alloy is usually produced by AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT.
The alloy is usually produced by AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT.
MATERIAL SPECIFICATIONS DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
Typical chemical compositions (mass fraction %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 13.5 ~ 15.5
Molybdenum, Mo (％): 0.20 ~ 1.20
Nickel, Ni (％): 1.00 ~ 2.50
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 13.5 ~ 15.5
Molybdenum, Mo (％): 0.20 ~ 1.20
Nickel, Ni (％): 1.00 ~ 2.50
Titanium, Ti (%): 0.30 ~ 0.50
Mechnical properties under room temp.
Condition: solution treatment
Thickness / mm: -
Tensile strength, σb / MPa: 650~850
Yield strength, σ0.2 ≥ MPa: 500
Elongation, δ5 ≥ (％): 30
Reduction of area, ψ ≥ (％): -
Yield strength, σ0.2 ≥ MPa: 500
Elongation, δ5 ≥ (％): 30
Reduction of area, ψ ≥ (％): -
Impact strength, Akv ≥ J: -
Hardness HBS30: 235max.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipments and parts.
Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt, nut and pressure vessel.
Mechanical parts used in the condition of corrosion resistance.
Bolt, nut and pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
PRODUCT PROFILE AND DIMENSIONS
Round bar / rod / disc (diameter): 6.0 to 800mm
Square bar / flat bar: 8 to 600mm
Round bar / rod / disc (diameter): 6.0 to 800mm
Square bar / flat bar: 8 to 600mm
Length: random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200 X W100 - 1500 X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6 X W60 - 1000 X L1000 - 2000mm
Steel strip via cold rolled: T0.3 - 3 X W5 - 200 X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Hot search：X5CrNiMoTi15-2
Previous page：1.4570 /DIN X6CrNiCuS18-9-2
Last page：1.4589 /DIN X5CrNiMoTi15-2
Total list
Monthly rank
- 21ASTM A565 type 616HT
- 18X8CrMnN20-10
- 142Cr11NiMoNbVN
- 13AM-350
- 13X66Cr13
- 13ASTM A693 Gr. XM-16
- 13SUH310
- 13S42035
- 132Cr20Mn9Ni2Si2N
- 12STS321