EN 10088-1 martensitic stainless steel 1.4935 (X20CrMoWV12-1) Creep-resistant steel 1.4935 peeled round bar, cold drawn flat bar, ESR, and forgings stock available
MATERIAL DESIGNATION - 1.4935 & X20CrMoWV12-1
Material category: 12%Cr - 1.0%Mo - 1.0%W - 0.25%V martensitic creep-resisting steels
Material specifications - DIN 17442, 17744, DIN EN 10302, 10095, EN 10088-1
Stock & Inventory - round bar diam.20 ~ 250mm, ESR ingot
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Customizing special material is welcome.
TYPICAL CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): 0.17 ~ 0.24
Silicon, Si (％): 0.10 ~ 0.50
Manganese, Mn (％): 0.30 ~ 0.80
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.015
Carbon, C (％): 0.17 ~ 0.24
Silicon, Si (％): 0.10 ~ 0.50
Manganese, Mn (％): 0.30 ~ 0.80
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.015
Cromium, Cr (％): 11.0 ～ 12.5
Nickel, Ni (％): 0.30 ~ 0.80
Molybdenum, Mo (％): 0.80 ~ 1.20
Nickel, Ni (％): 0.30 ~ 0.80
Molybdenum, Mo (％): 0.80 ~ 1.20
Vanadium, V (％): 0.20 ~ 0.35
Tungsten, W (%): 0.80 ~ 1.20
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: quenched and tempered
Tensile strength, Rm / MPa: 780 ~ 930
Condition: quenched and tempered
Tensile strength, Rm / MPa: 780 ~ 930
Yield strength, Rp0.2 ≥ MPa: 590
Elongation, A5 ≥ (％): 14.0
Elongation, A5 ≥ (％): 14.0
Hardness: HRC 25 ~ 30
Non-scale temperature in Air: 600℃
MANUFACTURING TECHNOLOGY - SMELTING
Heat resistant steel is generally smelt in electric arc furnace (EAF) or induction furnace (BEF). For higher quality, it should be smelt via technology of vacuum refining and external refining.
Heat resistant steel is generally smelt in electric arc furnace (EAF) or induction furnace (BEF). For higher quality, it should be smelt via technology of vacuum refining and external refining.
Martensitic heat resistant steels adopt hardening and tempering to stabilize the structure for excellent composite mechanical properties and high temperature strength.
PROFILE & DIMENSIONS AVAILABLE
Round bar / rod / disc (diameter): 6.0 ~ 950 mm
Square bar / flat bar: 8 ~ 600 mm
Heavy / middle plate via hot rolled: T10 ~ 400 X W60 ~ 1000 X Lmm
Round bar / rod / disc (diameter): 6.0 ~ 950 mm
Square bar / flat bar: 8 ~ 600 mm
Heavy / middle plate via hot rolled: T10 ~ 400 X W60 ~ 1000 X Lmm
Forging piece: stepped shafts, other different shapes based on OEM.
Hot search：1.4935
Previous page：X20CrMoWV12-1
Last page：X12CrNiMoV12-3 ESR
Total list
Monthly rank
- 21ASTM A565 type 616HT
- 18X8CrMnN20-10
- 142Cr11NiMoNbVN
- 13AM-350
- 13X66Cr13
- 13ASTM A693 Gr. XM-16
- 13SUH310
- 13S42035
- 132Cr20Mn9Ni2Si2N
- 12STS321