1.4418 QT900
2015-03-16 10:30:51 Origin: Remark:0 Click:
Martensitic series 1.4418 Round bar, Inventory 1.4418 QT900 Instock, Forgings, steelmaking, ESR, Hot forging/rolling, Heat treatment, Ultrasonic test, Technical Standards - BS EN 10088-3 (2005).
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
RAW MATERIAL SPECIFICATION - Grade 1.4418 QT900
MATERIAL CATEGORY - Stainless steel round bar, flat bars and forgings.
STEEL TYPE - Martensite series.
INVENTORY & STOCKLIST - Round bar diameter 22mm, 80mm, 115mm.
MATERIAL SPECIFICATIONS - BS EN 10083-3 (2005).
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (%): ≤ 0.06
Silicon, Si (%): ≤ 0.70
Manganese, Mn (%): ≤ 1.50
Phosphorus, P (%)≤: 0.040
Sulfur, S (%)≤: 0.030
Chromium, Cr (%): 15.0 ~ 17.0
Nickel, Ni (%): 4.00 ~ 6.00
Molybdenum, Mo (%): 0.80 ~ 1.50
Other (%): N ≥ 0.020
Silicon, Si (%): ≤ 0.70
Manganese, Mn (%): ≤ 1.50
Phosphorus, P (%)≤: 0.040
Sulfur, S (%)≤: 0.030
Chromium, Cr (%): 15.0 ~ 17.0
Nickel, Ni (%): 4.00 ~ 6.00
Molybdenum, Mo (%): 0.80 ~ 1.50
Other (%): N ≥ 0.020
MECHANICAL PROPERTY BASED ON THE DIFFERENT HEAT TREATMENT CYCLES
Thickness/≤mm: -
Condition of thermal treatment: annealed
Hardness HBS: 320
Yield strength σ0.2≥/MPa: -
Tensile strength σb/MPa: 1100
Elongation δ( longitudinal )≥(%): -
Elongation δ(transversal )≥(%): -
Impact absorbing power Akv≥/J| longitudinal: —
Impact absorbing power Akv≥/J| transversal : —
Condition of thermal treatment: annealed
Hardness HBS: 320
Yield strength σ0.2≥/MPa: -
Tensile strength σb/MPa: 1100
Elongation δ( longitudinal )≥(%): -
Elongation δ(transversal )≥(%): -
Impact absorbing power Akv≥/J| longitudinal: —
Impact absorbing power Akv≥/J| transversal : —
Thickness/≤mm: 60
Condition of thermal treatment: QT760
Hardness HBS: -
Yield strength σ0.2≥/MPa: 550
Tensile strength σb/MPa: 760~960
Elongation δ( longitudinal )≥(%): 16.0
Elongation δ(transversal )≥(%): -
Impact absorbing power Akv≥/J| longitudinal: 90
Condition of thermal treatment: QT760
Hardness HBS: -
Yield strength σ0.2≥/MPa: 550
Tensile strength σb/MPa: 760~960
Elongation δ( longitudinal )≥(%): 16.0
Elongation δ(transversal )≥(%): -
Impact absorbing power Akv≥/J| longitudinal: 90
Impact absorbing power Akv≥/J| transversal: -
Thickness/≤mm: 60<d≤250
Condition of thermal treatment: QT650
Hardness HBS: -
Yield strength σ0.2≥/MPa: 550
Tensile strength σb/MPa: 760~960
Elongation δ( longitudinal )≥(%): -
Elongation δ(transversal )≥(%): 14
Impact absorbing power Akv≥/J| longitudinal: -
Condition of thermal treatment: QT650
Hardness HBS: -
Yield strength σ0.2≥/MPa: 550
Tensile strength σb/MPa: 760~960
Elongation δ( longitudinal )≥(%): -
Elongation δ(transversal )≥(%): 14
Impact absorbing power Akv≥/J| longitudinal: -
Impact absorbing power Akv≥/J| transversal: 70
Thickness/≤mm: ≤160
Condition of thermal treatment: QT900
Hardness HBS: -
Yield strength σ0.2≥/MPa: 700
Tensile strength σb/MPa: 900~1100
Elongation δ( longitudinal )≥(%): 16
Elongation δ(transversal )≥(%): -
Impact absorbing power Akv≥/J| longitudinal: 80
Condition of thermal treatment: QT900
Hardness HBS: -
Yield strength σ0.2≥/MPa: 700
Tensile strength σb/MPa: 900~1100
Elongation δ( longitudinal )≥(%): 16
Elongation δ(transversal )≥(%): -
Impact absorbing power Akv≥/J| longitudinal: 80
mpact absorbing power Akv≥/J| transversal: -
Thickness/≤mm: 160<d≤250
Condition of thermal treatment: QT900
Hardness HBS: -
Yield strength σ0.2≥/MPa: 700
Tensile strength σb/MPa: 900~1100
Elongation δ( longitudinal )≥(%): 14
Elongation δ(transversal )≥(%): -
Impact absorbing power Akv≥/J| longitudinal: 60
Condition of thermal treatment: QT900
Hardness HBS: -
Yield strength σ0.2≥/MPa: 700
Tensile strength σb/MPa: 900~1100
Elongation δ( longitudinal )≥(%): 14
Elongation δ(transversal )≥(%): -
Impact absorbing power Akv≥/J| longitudinal: 60
Impact absorbing power Akv≥/J| transversal: -
AVAILABLE FORMS & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 - 12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Forging piece: stepped shafts, other different shapes based on OEM.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and Tempered.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and Tempered.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Previous page:BS X4CrNiMo16-5-1
Last page:X29CrS13
Total list
Monthly rank
- 33ASTM A565 Gr.616HT
- 26EN 57
- 26P550
- 25ASTM A890 Grade 4A
- 24AISI 306
- 22ASTM A638 Gr.660
- 19E-Z6NCT25
- 19SAE 51420
- 18ASTM A538 / AMS 6514
- 15GTD 450