Material specification stainless steel Cryogenic Tenelon datasheet,Cryogenic Tenelon Chemical, Ring forging, Bar, Wire rod, Sheet - steelmaking, Electroslag melting, Blooming, Ultrasonic test, Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - ASTM A276 or By agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION / DATASHEET - Cryogenic Tenelon
MATERIAL CATEGORY: Austenitic Stainless Steel bar
Technical standards: ASTM A276
CHEMICAL COMPOSITION (WEIGHT %)
C(%): ≤0.12
Si(%): ≤1.00
Mn(%): 14.0~16.0
P(%)≤: 0.060
S(%)≤: 0.030
Cr(%): 17.0~19.0
Ni(%): 5.00~6.00
Mo(%): —
Other(%): N 0.35~0.50
MECHANICAL PROPERTIES Si(%): ≤1.00
Mn(%): 14.0~16.0
P(%)≤: 0.060
S(%)≤: 0.030
Cr(%): 17.0~19.0
Ni(%): 5.00~6.00
Mo(%): —
Other(%): N 0.35~0.50
σb/MPa: 725 min.
σ0.2/MPa: 380 min.
δ(%): 40 min.
ф(%): -
δ(%): 40 min.
ф(%): -
Hardness (HBW): -
Hardness | HRB: -
Cold bending property: None
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Previous page:BS 304S61
Last page:Nitronic 40
Total list
Monthly rank
- 39ASTM A565 Gr.616HT
- 37X35CrMo17
- 30ASTM A638 Gr.660
- 28EN 58A
- 27Z10CNT18-11
- 26SAE 30304
- 26ASTM A538 / AMS 6514
- 26AISI 306
- 25Z15CN17-03
- 2410705MBU