ASTM B599 N08700
2015-09-23 09:33:48 Origin： Remark：0 Click：
Material specification N08700 datasheet, N08700 Chemical, Ring forging, N08700 Bar, N08700 Wire rod, sheet - steelmaking, ESR, Blooming, Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION / DATASHEET - N08700 /JS-700
MATERIAL CATEGORY: Austenitic stainless steel
Technical standards: ASTM B599
CHEMICAL COMPOSITION (WEIGHT %)
C(％): ≤0.040
Si(％): ≤1.00
Mn(％): ≤2.00
P(％)≤: 0.040
S(％)≤: 0.030
Cr(％): 19.0～23.0
Ni(％): 24.0~26.0
Mo(％): 4.30~5.00
Si(％): ≤1.00
Mn(％): ≤2.00
P(％)≤: 0.040
S(％)≤: 0.030
Cr(％): 19.0～23.0
Ni(％): 24.0~26.0
Mo(％): 4.30~5.00
Other (%): Cu ≤0.50, Nb ≤0.40
MECHANICAL PROPERTIES
Form: Plate, sheet, strip
Condition: annealed
σb/MPa: 550 min.
σ0.2/MPa: 240 min.
δ(％): 30 min.
ф(％): -
δ(％): 30 min.
ф(％): -
Hardness (HBW): -
APPLICATION FIELD
Food processing equipment
Heat exchangers
Hydrometallurgy
Oil and gas production equipment
Pulp mill bleach systems
Seawater handling equipment
Tall oil distillation columns and equipment
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
PRODUCT PROFILE
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
PRODUCT PROFILE
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.