Inventory Z12CNDV12 Round bar, Stocklist Z12CNDV12 Plate, Z12CNDV12 Property Steelmaking, ESR melted, Hot blooming forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3. Cold working, Polishing, Centerless grinding, Peeling or rough turned machining. Material technical specification AIR 9160/C - 1973.
TECHNICAL SPECIFICATION - AIR 9160C Grade Z12CNDV12
TECHNICAL SPECIFICATION: DGA - AIR 9160/C - 1973
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS
INVENTORY STOCKLIST - Diam.55 ~ 200mm
MATERIAL TYPE: Martensitic Stainless steel
CHEMICAL COMPOSITION (Mass Weight - %)
C (％): 0.08 ~ 0.15
Si (％): ≤ 0.35
Mn (％): 0.50 ~ 0.90
P (％) ≤: 0.035
S (％) ≤: 0.025
CHEMICAL COMPOSITION (Mass Weight - %)
C (％): 0.08 ~ 0.15
Si (％): ≤ 0.35
Mn (％): 0.50 ~ 0.90
P (％) ≤: 0.035
S (％) ≤: 0.025
Cr (%): 11.0 ~ 12.5
Mo (%): 1.50 ~ 2.00
Ni (%): 2.00 ~ 3.00
V (%): 0.25 ~ 0.40
N (%): 0.01 ~ 0.05
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength,σb/≥ MPa: 930 ~ 1140
Yield strength, σ0.2/≥ MPa: 780
Elongation, δ ≥(％): 14.0
Reduction of area, ф ≥ (％): 40.0
Impact, AK (J/cm2): -
Annealed hardness | HB: 286 min.
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength,σb/≥ MPa: 930 ~ 1140
Yield strength, σ0.2/≥ MPa: 780
Elongation, δ ≥(％): 14.0
Reduction of area, ф ≥ (％): 40.0
Impact, AK (J/cm2): -
Annealed hardness | HB: 286 min.
Quenching, 1050,+/-10 Deg, tempering 650, +/-5 Deg.
AVAILABLE FORMS & DIMENSIONS
Round bar (Diameter): 5.5 mm to 500mm
Square bar / Flat bar: 10mm to 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 200mm X Coil
Forging piece: stepped shafts with flanks / discs / tubes / slugs / donuts / cubes / other different shapes based on OEM.
AVAILABLE FORMS & DIMENSIONS
Round bar (Diameter): 5.5 mm to 500mm
Square bar / Flat bar: 10mm to 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 200mm X Coil
Forging piece: stepped shafts with flanks / discs / tubes / slugs / donuts / cubes / other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com