AQUAMET 17 is a precipitation-hardening martensitic stainless steel, combined with good toughness and corrosion resistance. AQUAMET 17 is used in pleasure boats, crew boats, fishing trawlers, patrol boats.
RAW MATERIAL SPECIFICATIONS - Grade Aquamet 17
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
Material category - Special alloys
Melting process - Consumable electrode remelted
Inventory & Stock list - Diam. 90mm / 95mm / 100mm / 120mm / 140mm / 160mm / 180mm.
HSN code for Customs - 72221100 / 72221900 / 72222000
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
Material category - Special alloys
Melting process - Consumable electrode remelted
Inventory & Stock list - Diam. 90mm / 95mm / 100mm / 120mm / 140mm / 160mm / 180mm.
HSN code for Customs - 72221100 / 72221900 / 72222000
MAIN CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.07
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%) ≤: 0.040
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 14.5 ~ 16.5
Nickel, Ni (%): 3.00 ~ 5.00
Molybdenum, Mo (%): -
Cobalt, Co (%): -
Copper, Cu (%): 3.00 ~ 5.00
Niobium, Nb (%): 0.15 ~ 0.45
MECHANICAL PROPERTIES AT ROOM TEMP.
Material supply condition: solution treated + aged
Tensile strength, σb/≥ MPa: 930
Yield strength, σ0.2/≥ MPa: 725
Elonghation, δ ≥(%): 15.0
Reduction of area, ф ≥ (%): 50.0
Hardness | HB: 277 Min.
AVAILABLE FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 10mm to 500mm
Hollow bar: OD200 - 1200 X ID120 - 1000 X H50 - 1000mm
Forging piece & Shaft: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our qualified production engineers, Email: sales@ccsteels.com.
Carbon, C (%): ≤ 0.07
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%) ≤: 0.040
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 14.5 ~ 16.5
Nickel, Ni (%): 3.00 ~ 5.00
Molybdenum, Mo (%): -
Cobalt, Co (%): -
Copper, Cu (%): 3.00 ~ 5.00
Niobium, Nb (%): 0.15 ~ 0.45
MECHANICAL PROPERTIES AT ROOM TEMP.
Material supply condition: solution treated + aged
Tensile strength, σb/≥ MPa: 930
Yield strength, σ0.2/≥ MPa: 725
Elonghation, δ ≥(%): 15.0
Reduction of area, ф ≥ (%): 50.0
Hardness | HB: 277 Min.
AVAILABLE FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 10mm to 500mm
Hollow bar: OD200 - 1200 X ID120 - 1000 X H50 - 1000mm
Forging piece & Shaft: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our qualified production engineers, Email: sales@ccsteels.com.
Total list
Monthly rank
- 67X35CrMo17
- 46AISI 306
- 46ASTM A565 Gr.616HT
- 37ASTM A890 Grade 4A
- 3410705MBU
- 34EN 58A
- 31Z15CN17-03
- 29Z50NMC12
- 27GTD 450 / C450
- 27ASTM A638 Gr.660