Magnadur 501
2021-04-06 09:14:35 Origin： Remark：0 Click：
Nonmagnetic Alloy Magnadur 501 Round bar, flat bar, Forgings Magnadur 501 ESR refined, Hot forging, Hot rolling, Heat treatment, 100% Ultrasonic flaw detection test, Cold machined.
TECHNICAL DATA SHEET - Grade Magnadur 501
TECHNICAL SPECIFICATIONS: By agreement
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic stainless steel bar and plate
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): 0.30 ~ 0.60
Manganese, Mn (％): 18.5 ~ 22.0
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.008
Chromium, Cr (％): 13.0 ~ 16.0
Nickel, Ni (％): 0.25 ~ 0.50
Molybdenum, Mo (%): 0.35 ~ 0.60
Nitrogen, N (%): 0.32 ~ 0.40
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic stainless steel bar and plate
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): 0.30 ~ 0.60
Manganese, Mn (％): 18.5 ~ 22.0
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.008
Chromium, Cr (％): 13.0 ~ 16.0
Nickel, Ni (％): 0.25 ~ 0.50
Molybdenum, Mo (%): 0.35 ~ 0.60
Nitrogen, N (%): 0.32 ~ 0.40
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: anneal treated 1050 ~ 1150 Deg.C
Tensile strength, σb/ ≥ MPa: 900
Yield strength, σ0.2/ ≥ MPa: 770
Elongation, δ (％) ≥: 25.0
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 277 Min.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Tensile strength, σb/ ≥ MPa: 900
Yield strength, σ0.2/ ≥ MPa: 770
Elongation, δ (％) ≥: 25.0
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 277 Min.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 350mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 600mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Round bar (Diameter): 5.5 ~ 350mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 600mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar