STS 630 H1025 Stockist, STS 630 H1025 Equivalent Steel

STS 630 H1025
2022-07-22 10:31:13   Origin:   Remark:0 Click:

Flat bars STS 630 strip, STS 630 aged H1025 Inventory, Plate STS 630 H1025 Forgings Stocklist Properties Technical specifications - KS D3705 - 2001 / 2006. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
RAW MATERIAL SPECIFICATIONS - Grade STS 630 H1025
Technical Specifications - KS D3705 - 2001 / 2006
Official Test Certificate - issued by TUV - SGS -  BV
HS Code For Customs - 72201100 / 72202030 / 72221100
Material Category - Hot / cold rolled Stainless steel sheet, strip
Inventory & Stocklist - Round bar dia.10 ~ 220mm, sheet / plate 3.0 ~ 20 X 5000 ~ 1200 X L mm 
Chemical Composition (Mass Weight - %)
C (%):     
≤ 0.07
Si (%):    ≤ 1.00
Mn (%):  ≤ 1.00
P (%) ≤:  0.040
S (%) ≤:  0.030
Cr (%):    15.0 ~ 17.0
Ni (%):    3.00 ~ 5.00
Cu (%):   3.00 ~ 5.00
Nb (%):   0.15 ~ 0.45
MECHANICAL PROPERTY UNDER DIFFERENT HEAT TREATMENT CYCLE
Condition: solution 1050 ℃, oil / air cooling.
Ageing treatment: H900 / H1025 / H1075 / H1150
Tensile strength, σb/ ≥ MPa: 1310 / 1070 / 1000 / 930
Yield strength, σ0.2/ ≥ MPa: 1175 / 1000 / 865 / 725
Elongation, δ (%) ≥: 10.0 / 12.0 / 13.0 / 16.0
Reduction of area, ф (%) ≥: -
Hardness under anneal ≤ (HBW): 365
MELTING PROCESS
The alloy is usually produced by AOD / EAF or VIM followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PROFLE & DIMENSIONS
Round bar (Diameter): 5.5 ~ 650mm
Strip / Plate (Thickness X width X Length): 1.0 ~ 2.5mm X 10 ~ 1200mm X Lmm
Flat bar (Thickness X Width): 4 ~ 300 X 15 ~ 550mm
Length: random length, fixed length or based on the customer's special requirement.