AMS 5687
2023-03-15 07:57:09   Origin：   Remark：0 Click：

MATERIAL TECHNICAL DATASHEET - Grade AMS 5687
Material Category - Aerospace Material Steel Series
Techncial Specifications - AMS 5687N
HS Code for Customs - 72221100 / 72221900 / 72223000
Official Test Report - issued by TUV - SGS - BV
MAIN CHEMICAL COMPOSITIONS (mass weight %) 
Carbon, C (％):  ≤ 0.15
Manganese, Mn (％):  ≤ 1.00
Silicon, Si (％):  ≤ 0.50
Phosphorus, P (％)≤:  0.030
Sulfur, S (％)≤:  0.025
Chromium, Cr (％):  14.0 ~ 17.0
Nickel, Ni (％):  72.0 min.
Niobium,, Cb (%): ≤ 1.0
Titanium, Ti (%): ≤ 0.50
Aluminum,, Al (%): ≤ 0.35
Tantalum,, Ta (%): ≤ 0.05
Copper, Cu (%): ≤ 0.50
Ferrum, Fe (%): 6.00 ~ 10.0
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: cold drawn from hot finished wire or rod, annealed.
Tensile strength, σb/MPa: 758 MPa. max. (Coiled or spooled)
Yield strength, σ0.2/MPa:  -
Elongation, δ(％):  -
Reduction of area, ф (％):  -
Hardness under hot finished condition | HBW:  -
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on. These products have been used typically for parts requiring both corrosion and oxidation resistance.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Round bar (Diameter): 5.5 to 300mm
Wire rod (diameter): 1.50 ~ 5.5mm
Square bar / Flat bar (Thickness X width): 10 to 600mm
Length: fixed length, random length, or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.