Nitronic 30
2020-04-27 10:36:54 Origin： Remark：0 Click：
Specifications Nitronic 30 Ex-stock,Nitronic 30 Chemical, Nitronic 30 mechanical properties from Steelmaking,ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire.
TECHNICAL DATA SHEET - Grade Nitronic 30
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenitic stainless steel
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.03
Si (％): ≤ 1.00
Mn (％): 7.00 ~ 9.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 15.0 ~ 17.0
Ni (％): 1.50 ~ 3.00
Mo (％): -
Si (％): ≤ 1.00
Mn (％): 7.00 ~ 9.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 15.0 ~ 17.0
Ni (％): 1.50 ~ 3.00
Mo (％): -
W (%): -
Cu (%): ≤ 1.00
Ti (%): -
Co (%): -
N (％): 0.15 ~ 0.30
N (％): 0.15 ~ 0.30
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 758
Yield strength, σ0.2/≥ MPa: 380
Elongation, δ ≥(％): 50
Elongation, δ ≥(％): 50
Reduction of area, ф ≥ (％): -
Hardness | HRB: B95
APPLICATION FIELD
Tall oil distillation columns and equipments
Food processing equipments
Hydrometallurgy, heat exchangers
Oil and gas production equipments
Pulp mill bleach systems
Seawater handling equipments
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by BEF / AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD30 - 1200mm, with wall thickness ranging from 15 to 350 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD30 - 1200mm, with wall thickness ranging from 15 to 350 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Previous page：A182 Gr. S42900
Last page：ASTM 403Cb
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17