Nitronic 33 / S24000
2015-07-01 09:08:01 Origin： Remark：0 Click：
ASTM A276 Specification Austenitic Steel Nitronic 33 Flat bar, Round bar, Plate S24000 Ring forging, Nitronic 33 Round Bar, Cold worked, Heat treatment.
TECHNICAL DATA SHEET - Grade Nitronic 33 & S24000
MATERIAL CATEGORY - Austenitic Stainless Steel
TECHNICAL SPECIFICATIONS - ASTM A276, A580
MELTING PROCESS - Consumable electrode remelted
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
STOCKLIST & INVENTORY: Diameter 60 ~ 130mm
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 0.75
Manganese, Mn (％): 11.5 ~ 14.5
Phosphorus, P (％)≤: 0.060
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 17.0 ~ 19.0
Nickel, Ni (％): 2.25 ~ 3.75
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.20 ~ 0.40
MATERIAL CATEGORY - Austenitic Stainless Steel
TECHNICAL SPECIFICATIONS - ASTM A276, A580
MELTING PROCESS - Consumable electrode remelted
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
STOCKLIST & INVENTORY: Diameter 60 ~ 130mm
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 0.75
Manganese, Mn (％): 11.5 ~ 14.5
Phosphorus, P (％)≤: 0.060
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 17.0 ~ 19.0
Nickel, Ni (％): 2.25 ~ 3.75
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.20 ~ 0.40
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile Strength, σb/MPa: 689 min.
Yield Strength, σ0.2/MPa: 379 min.
Elongation, δ (％): 40 min.
Reduction of area, ф(％): -
Elongation, δ (％): 40 min.
Reduction of area, ф(％): -
Hardness (HBW): 241
Hardness | HRB: -
Cold bending property: None
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PROFILE & DIMENSION
Round bar / Wire rod (Diameter1): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PROFILE & DIMENSION
Round bar / Wire rod (Diameter1): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 500mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com
Hot search：Nitronic 33 / S24000
Previous page：AMS 5656
Last page：XM-19 / Nitronic 50
Total list
Monthly rank
- 252Cr12NiMo1W1V
- 2410705MBU
- 21X4CrNi13-4
- 19A564 Grade XM-13
- 18ASTM A768 Grade 2
- 16S137
- 1610705BA
- 16St T17/13W
- 12Z50NMC12
- 121.4906