Nitronic 19D / S32001
2015-07-02 10:05:06 Origin： Remark：0 Click：
Specification Nitronic 19D Datasheet, Inventory Nitronic 19D Chemical, Suppliers Nitronic 19D Ring forging, Bar, Wire rod, Sheet - steelmaking, Nitronic 19D /S32001 Electroslag melting, Blooming, Ultrasonic test, Forging, Rolling, Heat treatment, Straightened, Nitronic 19D/S32001 Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.Technical Standards - ASTM A240 or By agreement
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATA SHEET - Nitronic 19D & S32001
MATERIAL CATEGORY - Austenite-Ferrite / duplex stainless steel
Technical standards - ASTM A240. A789
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): 4.00 ~ 6.00
P (％)≤: 0.030
S (％)≤: 0.020
Cr (％): 19.5 ~ 21.5
Ni (％): 1.00 ~ 3.00
Mo (％): ≤ 0.60
N (%): 0.05 ~ 0.17
Other (％): Cu ≤ 1.00
Si (％): ≤ 1.00
Mn (％): 4.00 ~ 6.00
P (％)≤: 0.030
S (％)≤: 0.020
Cr (％): 19.5 ~ 21.5
Ni (％): 1.00 ~ 3.00
Mo (％): ≤ 0.60
N (%): 0.05 ~ 0.17
Other (％): Cu ≤ 1.00
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Annealed condition
Tensile strength, σb/MPa: 620 min.
Yield strength, σ0.2/MPa: 450 min.
Elongation, δ (％): 25.0 min.
Reduction of area, ф (％): -
Elongation, δ (％): 25.0 min.
Reduction of area, ф (％): -
Hardness (HBW): -
PROFILE AND DIMENSIONS
Round bar / Wire rod (Diameter1): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W60 - 1200mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
APPLICATION FIELD
Chemical processing equipment
Desalination equipment
Flue gas desulfurization scrubbers
Food processing equipment
Heat exchangers
Hydrometallurgy
Oil and gas production equipment
Pulp mill bleach systems
Seawater handling equipment
Tall oil distillation columns and equipment
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
Hot search：Nitronic 19D / S32001
Previous page：Grade 253MA /S30815
Last page：S67
Total list
Monthly rank
- 261.4418 QT900
- 23GTD 450
- 171.3952
- 17SAE 51410
- 16AISI 630 (17-4PH)
- 15S144
- 15ASTM A182 Gr.F6NM
- 14St T17/13W
- 131.4112
- 13Z5CNU17-4PH