Nitronic 20
2016-08-26 11:35:50 Origin： Remark：0 Click：
Exhaust valve Steel Nitronic 20 Round bar, flat bar, wire rod Nitronic 20 instock Remelted, Blooming, Hot forging/rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working.
TECHNICAL DATA SHEET - Grade Alloy Nitronic 20
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: SAE / UNS system exhaust valve Steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.28 ~ 0.38
Silicon, Si (％): 0.60 ~ 0.90
Manganese, Mn (％): 1.50 ~ 3.50
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 22.0 ~ 24.0
Nickel, Ni (％): 7.00 ~ 9.00
Molybdenum, Mo (％): -
Manganese, Mn (％): 1.50 ~ 3.50
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 22.0 ~ 24.0
Nickel, Ni (％): 7.00 ~ 9.00
Molybdenum, Mo (％): -
Nitrogen, N (%): 0.28 ~ 0.35
MECHANICAL PROPERTIES AT ROOM TEMP.
Condition: Quenched and tempered
Tensile strength, σb/≥ MPa: 850
Yield strength, σ0.2/≥ MPa: 550
Elongation, δ ≥(％): 25.0
Elongation, δ ≥(％): 25.0
Reduction of area, ф ≥ (％): -
Hardness | HB: -
FEATURES AND CLASSIFICATIONS
Valve steel is a subbranch of heat resistant steels, which is a special material for processing the vent valve & intake valve of combustion engines. This steel material is always under the high temperature 450 ~ 900℃ and also in the operating conditions of 3000~7000kPa explosion pressure. It longly stands up to the gas-fired high temperature corrosion, scouring of gasoline, diesel and also friction from valve seats. Hence, the valve steel material must have enough heat resistance, high temperature resistance corrosivity, inoxidizability, abrasive resistance and impact resistance under the highest working temperature.
Valve steel (gas valve steel) is suit for fabricating different types of valves. To improve the abrasive resistance and corrosion resistance, surface modified process can be used, such as surface alumetizing, bead welding hard alloy. Based on the pattern of organization, Valve steel is divided into martensitic type and austenitic type. The presentative martensitic valve steel is BS 381S34, BS 349S52 and austenitic valve steel BS 401S45, BS 443S65.
Valve steel (gas valve steel) is suit for fabricating different types of valves. To improve the abrasive resistance and corrosion resistance, surface modified process can be used, such as surface alumetizing, bead welding hard alloy. Based on the pattern of organization, Valve steel is divided into martensitic type and austenitic type. The presentative martensitic valve steel is BS 381S34, BS 349S52 and austenitic valve steel BS 401S45, BS 443S65.
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 10mm to 500mm
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 - 5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
Square bar / Flat bar: 10mm to 500mm
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 - 5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Previous page：EV16/EMS 235
Last page：S63018
Total list
Monthly rank
- 27X11CrMo12-1
- 2710705MBU
- 21S165M / S165
- 20AISI 306
- 20X35CrMo17
- 18P550
- 18Z10CNT18-11
- 17ASTM A565 Gr.616HT
- 16AISI 630 (17-4PH)
- 16S42400