UNS S32506 Stockist, UNS S32506 Equivalent Datasheet

UNS S32506
2014-09-28 11:04:50   Origin:   Remark:0 Click:

Description S32506 Inventory, Suppliers S32506 Stocklist, Forging S32506 Ex-stock & Plate Heat treatment Machined, Rod Exporters Ex-stock Sale - Technical standards - ASTM A182 - 2018.or by agreement.100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL DATA SHEET - Alloy Steel UNS S32506
MATERIAL CATEGORY: 25Cr-7Ni-3Mo-W-N Austenite-Ferrite type
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
AVAILABILITY
Round bar / flat bar / hollow bar / forgings
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
PROFILE AND DIMENSIONS 
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 200mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
CHEMICAL COMPOSITION (Mass weight - %)
C (%):     ≤ 0.030
Si (%):    ≤ 0.90
Mn (%):   ≤ 1.00
P (%)≤:   0.040
S (%)≤:   0.015
Cr (%):    24.0 ~ 26.0
Ni (%):    5.50 ~ 7.20
Mo (%):   3.00 ~ 3.50
N (%):     0.08 ~ 0.20 
W (%):    0.05 ~ 0.30
MECHANICAL PROPERTIES UNDER FINAL HEAT TREATMENT
Tensile strength, σb/MPa: 620
Yield strength, σ0.2/MPa:  450
Elongation, δ (%): 18.0
Reduction of area, ф (%):  
Hardness | HRC(HBW): 302 (32HRC)
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of
stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:
sales@ccsteels.com

Hot search:UNS S32506

Previous page:UNS S32304
Last page:S32520

Share to: