AMS 5616
2020-11-10 08:25:36 Origin： Remark：0 Click：
Description AMS 5616 Round bars, Ex-stock AMS 5616 Strip, Stocklist AMS 5616 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade AMS 5616
MELTING: Consumable electrode remelted steel
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (Mass weight - %)
C (％): 0.15 ~ 0.20
Si (％): ≤ 0.50
Mn (％): ≤ 0.50
P (％)≤: 0.025
S (％)≤: 0.015
Cr (％): 12.0 ~ 14.0
Ni (％): 1.80 ~ 2.20
Mo (％): ≤ 0.50
W (％): 2.50 ~ 3.50
Si (％): ≤ 0.50
Mn (％): ≤ 0.50
P (％)≤: 0.025
S (％)≤: 0.015
Cr (％): 12.0 ~ 14.0
Ni (％): 1.80 ~ 2.20
Mo (％): ≤ 0.50
W (％): 2.50 ~ 3.50
Al (%): ≤ 0.15
Cu (%): ≤ 0.50
N (%): ≤ 0.08
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Tensile strength, σb ≥/MPa: 1034
Yield strength, σ0.2 ≥/MPa:-
Yield strength, σ0.2 ≥/MPa:-
Elongation, δ ≥(％): 10.0
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤ 311 (annealed condition)
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤ 311 (annealed condition)
Condition of heat treatment: HT 981℃ ~ 1080℃ air or oil cooled, ≥620℃ X 2H, two times tempered
Tensile strength, σb ≥/MPa: 965
Yield strength, σ0.2 ≥/MPa: 760
Yield strength, σ0.2 ≥/MPa: 760
Elongation, δ ≥(％): 15.0
Reduction of area, ф ≥(％): 45.0
Hardness | HBW: 302 ~ 352
Reduction of area, ф ≥(％): 45.0
Hardness | HBW: 302 ~ 352
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 500mm
Square bar / Flat bar: 10mm to 450mm
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 500mm
Square bar / Flat bar: 10mm to 450mm
Wire rod: 1.0mm to 13.0mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Total list
Monthly rank
- 43ASTM A890 Grade 4A
- 33Z15CN17-03
- 292Cr12NiMo1W1V
- 27GTD 450
- 27AISI 306
- 22X12CrNi18-8
- 21P550
- 19Z10CNT18-11
- 18E-Z6NCT25
- 18St T17/13W